|Stress Corrosion can Leads to Detachment of Diamond-Like Carbon (DLC) Nano Layer|
For the artificial joints, the coatings often fail because they detach.
Some researchers of Empa found out the cause. They developed methods to both make the interface between the DLC layer and the metal underneath corrosion-resistant and to predict the lifetime of the implants.
Whether on computer hard disks, saw blades, embossing tools, razor blades or fuel-injection nozzles, extremely hard coatings made of diamond-like carbon (DLC) have proven their value over and over again. They reduce wear and thereby give tools and components a longer operating lifetime. What could be more logical than to apply DLC to medical implants such as artificial joints, reasoned a number of implant manufacturers. After all, wear is a problem there, too.
The diamond-like carbon has subsequently withstood endless in vitro tests in several manufacturers’ laboratories and has shown itself to be well tolerated by human tissue, extremely hard wearing, and resistant to the relatively aggressive environment in the human body. Despite this, when DLC-coated joints were first implanted into human patients, serious problems arose after only a few years. The DLC coatings were not worn away, but rather they detached from the implant material for no apparent reason.
In a project financed by the Swiss Innovation Promotion Agency (CTI) together with the medical technology company Synthes and the coating company Ionbond AG, Empa researchers sought out the cause of this detachment. For this, the researchers conducted detailed studies of the interface between the implant material and the coating. "When two materials are placed in contact with each other, the result is a reaction layer at the interface between them, which is only several atomic layers thick. Thus a new material is formed, which we investigated now for the first time", explains Roland Hauert of Empa's "Nanoscale Materials Science" laboratory.
It had been shown that the so far barely considered reaction layer, which is not always completely corrosion resistant, is responsible for the detachment of the DLC layer. On the one hand, stress corrosion cracking occurred in the reaction layer. The mechanical load in conjunction with the penetration of body fluids led to slow-growing cracks, which in turn caused the DLC substrate to detach little by little.
The Empa team, together with their industry partners Synthes and Ionbond, developed a corrosion-resistant intermediate layer at the interface to the DLC layer. They also developed a process that can determine a crack’s growth rate under conditions similar to those experienced in the human body as well as the dissolution rate of the reaction layer in cases of crevice corrosion. "This then allows us to calculate the expected operating lifetime of the coated implant in the human body", says Roland Hauert. Whether or not a DLC-coated implant will fail prematurely in vivo can henceforth already be determined during the development of the product.
Reference: www.azonano.com, www.empa.ch
|Chemicals and Raw Materials|
|Coating Application Equipment for Pipeline|
|Cooling Water System|
|Corrosion & Electrochemical Instruments|
|Corrosion Probes, Coupons and Holders|
|Industrial Coatings and Sealants|
|Laboratory Testing Services|
|Manufacturing and Process Equipment|
|Manufacturing Cells and Systems|
|Optical Components and Optics|
|Surface and Corrosion Protection Products|
|Test and Measurement Equipment|